3D model (JSmol)
CompTox Dashboard (EPA)
|Melting point||1,132 °C (2,070 °F; 1,405 K)|
|Boiling point||1,950 °C (3,540 °F; 2,220 K) sublimates|
|sublimates at 1275 °C|
|reacts violently to form NaOH|
|Solubility||reacts with ethanol|
|Antifluorite (face centered cubic), cF12|
|Fm3m, No. 225|
|Tetrahedral (Na+); cubic (O2-)|
Heat capacity (C)
Std enthalpy of
Gibbs free energy (ΔfG?)
|Main hazards||corrosive, reacts violently with water|
|Safety data sheet||ICSC 1653|
|NFPA 704 (fire diamond)|
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
|what is ?)(|
Sodium oxide is a chemical compound with the formula Na2O. It is used in ceramics and glasses. The compound is the base anhydride of sodium hydroxide; when water is added to sodium oxide, NaOH is produced.
The alkali metal oxides M2O (M = Li, Na, K, Rb) crystallise in the antifluorite structure. In this motif the positions of the anions and cations are reversed relative to their positions in CaF2, with sodium ions tetrahedrally coordinated to 4 oxide ions and oxide cubically coordinated to 8 sodium ions.
Most of these reactions rely on the reduction of something by sodium, whether it is hydroxide, peroxide, or nitrite.
A more accessible way of producing it in the laboratory consists in decomposing sodium ascorbate at temperatures over 209 Celsius degrees.
Sodium oxide is a component of most glass, although it is added in the form of "soda" (sodium carbonate). Typically, manufactured glass contains around 15% sodium oxide, 70% silica (silicon dioxide) and 9% lime (calcium oxide). The sodium carbonate "soda" serves as a flux to lower the temperature at which the silica mixture melts. Soda glass has a much lower melting temperature than pure silica, and has slightly higher elasticity. These changes arise because the silicon dioxide and soda have reacted to form sodium silicates of the general formula Na2[SiO2]x[SiO3].